Odovtos International Journal of Dental Sciences

On-line version ISSN 2215-3411Print version ISSN 1659-1046

Odovtos vol.24 n.2 San José May./Aug. 2022

http://dx.doi.org/10.15517/ijds.2021.47335 

Basic research

In Vitro effect of denture cleansers on the color stability of polyetheretherketone and other denture base polymers

Efecto in vitro de los limpiadores de prótesis en la estabilidad del color de la polieteretercetona y otros polímeros base de prótesis

1Assistant Professor, Department of Prosthodontics, Faculty of Dentistry, Firat University, Elazig, Turkey. https://orcid.org/0000-0001-8883-8307

Abstract

The aim of this in vitro study was to compare the long-term effect of overnight use of denture cleansers with different chemical compositions on the color stability of denture base polymers (DBPs). The four DBPs evaluated were PEEK (PK group), thermoinjection-molded polyamide (PA group), auto-polymerized polymethylmethacrylate (PMMA) (AP group), and heat-polymerized resin PMMA (HP group). The cleaning agents used were Corega tablet (CT), Protefix tablet (PT), and 0.5% sodium hypochlorite (NaOCl) solution (SH). Distilled water (DW) served as a control. Forty-eight disc-shaped specimens (10mm × 2mm) were prepared from each DBP and randomly immersed in the different storage media (n=12 in each group). Color measurements of the specimens before and after immersion in the denture cleansers were made using a spectrophotometer (VITA Easyshade V). The color changes were measured and recorded in L* a* b*. After 120 d, the CIEDE2000 formula was used to calculate color changes (ΔE00). For analysis of the data, a multivariate analysis of variance was used (p<0.05). The results of the statistical analysis revealed significant color change differences in the DBPs immersed in the various denture cleansers (p<0.05). Groups PA and PK showed the highest values for all solutions. AP-SH showed the highest ΔE00 value in group AP, no significant difference was found between other solutions. In group HP, there was no statistically significant difference between the average ΔE00 values of all solutions. Long-term daily use of the denture cleansers affected the color stability of all the DBPs, although the level of color change was acceptable. Laboratory and clinical studies on the color stability of PEEK are needed to confirm the results of this study.

Keywords Color stability; Denture base material; PEEK; PMMA; Polymer

Resumen

El objetivo de este estudio in vitro fue comparar el efecto a largo plazo del uso nocturno de limpiadores de prótesis con diferentes composiciones químicas sobre la estabilidad del color de los polímeros base de prótesis (DBP). Los cuatro DBP evaluados fueron PEEK (grupo PK), poliamida moldeada por termoinyección (grupo PA), polimetilmetacrilato (PMMA) autopolimerizado (grupo AP) y resina PMMA termopolimerizada (grupo HP). Los agentes de limpieza utilizados fueron Corega (CT), Protefix (PT) y la solución de hipoclorito de sodio (NaOCl) al 0,5% (SH). El agua destilada (DW) sirvió de control. Se prepararon 48 especímenes en forma de disco (10mm × 2mm) de cada DBP y se sumergieron al azar en los diferentes medios de almacenamiento (n=12 en cada grupo). Las mediciones del color de las muestras antes y después de la inmersión en los limpiadores de dentaduras se realizaron con un espectrofotómetro (VITA Easyshade V). Los cambios de color se midieron y registraron en L* a* b*. Después de 120 d, se utilizó la fórmula CIEDE2000 para calcular los cambios de color (ΔE00). Para el análisis de los datos, se utilizó un análisis multivariante de la varianza (p<0,05). Los resultados del análisis estadístico revelaron diferencias significativas en el cambio de color de los DBP sumergidos en los distintos limpiadores de dentaduras (p<0,05). Los grupos PA y PK mostraron los valores más altos para todas las soluciones. AP-SH mostró el valor ΔE00 más alto en el grupo AP, no se encontraron diferencias significativas entre las demás soluciones. En el grupo HP, no hubo diferencias estadísticamente significativas entre los valores medios de ΔE00 de todas las soluciones. El uso diario a largo plazo de los limpiadores de dentaduras afectó a la estabilidad del color de todos los DBP, aunque el nivel de cambio de color fue aceptable. Se necesitan estudios de laboratorio y clínicos sobre la estabilidad del color del PEEK para confirmar los resultados de este estudio.

Palabras clave Estabilidad de color; Material de base para prótesis; PEEK; PMMA; Polímero

Introduction

Polymethylmethacrylate (PMMA) and polya- mides are frequently used in partial or complete removable dentures (1,2). Of the two, owing to its low density, esthetics, low cost, and ease of manipulation, PMMA has long been the preferred material in removable prostheses. However, PMMA also has disadvantages, such as water sorption, solubility, insufficient impact and bending strengths, residual monomer release, and polymerization shrinkage. Various efforts have been made to overcome the disadvantages of PMMA-based composites, including the addition of epoxy resins, polyamide, or butadiene styrene (2).

The elasticity of polyamides is higher than that of heat-polymerized PMMA. High elasticity is required to ensure resistance to impacts and breakage. As compared to heat-polymerized PMMA, polyamides have various advantages, including reduced polymerization shrinkage and deformation. In terms of their toxicological safety, they can be used in patients with allergies to residual monomers (3). However, polyamide materials also suffer from problems, such as water sorption, surface roughness, bacterial contamination, and discoloration. Furthermore, they are difficult to polish (4).

Due to the disadvantages associated with the use of metal frameworks in partial or complete removable prostheses, metal-free materials, including high-performance polymers, such as arylketone polymers, have been studied (5,6). A number of studies confirmed that polymer-based frameworks exhibited better esthetics (translucency and color), lower cost, higher elasticity, improved lightness than metal frameworks. Other reported advantages of polymer-based frameworks included ease of production and repair (4,5,6,7,8). Polymers were reported to be particularly advan- tageous in removable prostheses owing to issues relating to design control and repeatable and precise production potential using computer-assis- ted design (CAD)/computer assisted manufacturing (CAM) systems.

PEEK, a recently developed polymer belon- ging to the polyaryletherketone family, has mecha- nical and physical properties similar to those of bone and tooth hard tissues (6). This polymer has properties such as elimination of allergic reactions and metallic taste, polishability, low plaque affinity and good wear resistance (9). More research on the use of polymers in partial or complete remova- ble dentures is needed.

Dental prosthesis hygiene and oral mucosal health are extremely important in implant-supported and tooth-supported removable prostheses to combat oral and systemic infections, especially in geriatric and immuno-compromised patients (1,10). Thus, dental prostheses must be cleaned properly on a regular basis. Cleaning with chemical solutions can contribute to oral health, prosthetic denture life, and overall quality of life. Denture cleaning agents are divided into different groups according to their chemical compositions (i.e., enzymes, acids, hypochlorites, and peroxides) (1,11). Denture cleaning agents with different chemical compositions are widely used in the market to prevent microorganism colonization and plaque formation, especially Candida species, without changing the physical and mechanical properties of the prosthetic material (12). Ideally, denture base polymers (DBPs) should contain insolu- ble components and exhibit low water sorption, as these materials are exposed to saliva, food, water, and cleansers, resulting in water sorption and loss of soluble components. Over time, exposure to these factors results in surface erosion of the prosthetic material, with resulting effects on the color stability and esthetic appearance of the prosthesis (13).

Previous studies have evaluated the shortterm use of high concentrations of sodium hypochlorite (NaOCl) as a denture cleaning agent (14,15). For denture cleansers used daily and long term, agents with low concentrations of NaOCl are needed (16,17). A number of studies have investigated the effect of cleansers with different NaOCl contents on DBPs in terms of their color stability, water sorption, hardness, roughness, and solubility (1,3,10-20). Most of these color stability studies used the CIELab formula (ΔEab) to determine color differences (1,13,20). However, a new formula, CIEDE2000 (ΔE00), has been proposed to replace the ΔEab formula for calculating color differences from L* a* b* values. According to a number of studies, ΔE00 values are superior to ΔEab values in terms of detecting small color differences, especially visual differences in high chroma colors (21,22,23,24). For this reason, we used the CIEDE2000 formula for calculating color changes in our study.

There are insufficient studies on the longterm effects of cleansers on the color stability and optical properties of PEEK polymers are insufficient. In a previous study, color stability in different colorant media was evaluated on PEEK, PMMA and composite resin for a short time. Subsequently, the color change of the cleaning methods was evaluated (20). Another study evaluated the long-term effect of staining and cleaning solutions on color stability in polyoxymethylene and PMMA (25). The aim of this in vitro study was to compare the effects of long-term use of effervescent tablets, and 0.5% NaOCl solution on the color stability of PEEK, thermoinjection-molded polyamide, auto-polymerized, and heat-polymerized PMMA polymers. The null hypothesis was that the different cleansers would not affect the color stability of the DBPs.

Materials and methods

Group allocation

Forty-eight disc-shaped specimens (10mm×2mm) were prepared from each DBP (n=48) and randomly divided into four different storage media subgroups (n=12): Corega tablet ((CT), (Stafford-Miller Limited, Waterford, Ireland), Protefix tablet ((PT), (Queisser Pharma, Flensburg, Germany)), 0.5% NaOCl solution ((SH), (Aklar Kimya, Ankara, Turkey)), and distilled water (DW) as a control. Table 1 provides information on the compositions of the materials and the manufacturers of the prosthetic materials and denture cleaning solutions used in the study.

In each of the AP, HP, and PA groups, 144 disc-shaped wax samples (Cavex Set Up Regular; Cavex, Haarlem, Netherlands) were created in metal molds (thickness: 2mm; diameter: 10mm). In the AP group, the specimens were prepared in the powder liquid ratio recommended by the manufacturer. In the HP group, the specimens were polymerized under pressure in a hot water bath at 100°C for 45min. In the PA group, the specimens were melted at temperatures of between 270 and 288°C for 11min according to the manufacturers recommendations and then injected into a muffle for 3min at 6 bar pressure for 30sec. After polymerization, all the specimens were kept in DW for 24h at 37°C for residual monomer elimination. Excess resin was trimmed using a hand piece with a tungsten steel bur at low speed. In the PK group, the specimens were designed using stereolithography (STL) and AutoCAD (Autodesk, San Rafael, CA, USA). The STL files were transferred to a CAD/ CAM milling machine (Ceramill Motion 2; Amann Girrbach AG, Koblach, Austria), and the specimens were milled from a PEEK dental disk (Juvora Dental Disc; Juvora, London, U.K.).

The surfaces of all the specimens were polished with 600-grit, 800-grit, and 1200-grit waterproof silicon carbide paper (Struers, Ballerup, Denmark) using a polishing device (Phoenix Beta; Buehler, IL, U.S.A.) under running water. They were then polished with a high-gloss agent (KMG; Candulor AG, Zurich, Switzerland). A digital caliper (Digimatic Caliper; Mitutoyo Corporation, Kanagawa, Japan) was used to ensure a uniform specimen thickness of 2mm. Subsequently, the specimens were cleaned ultrasonically for 10min and dried with a paper towel.

Table 1 Commercial names, compositions, and manufacturers of the materials used in the study. 

Product Code Type and Components Manufacturer
SR Triplex Hot HP Heat-polymerized PMMA Ivoclar Vivadent AG., Schaan, Leichens- tein
SR Triplex Cold AP Auto-polymerized PMMA Ivoclar Vivadent AG., Schaan, Leichens- tein
Deflex PA Injection molded polyamide Nuxen SRL, Buenos Aires, Argentina
PEEK PK Unfilled PEEK CAD/CAM disc Juvora Dental Disc; Juvora, London, UK
Corega Tablet CT Potassium Monopersulfate; Sodium Bicarbonate; Sodium Lauryl Sulfoacetate; Sodium Perborate Monohydrate; Sodium Polyphosphate Stafford-Miller Limited, Waterford, Ireland
Protefix Tablet PT Sodium bicarbonate, Potassium caroate, Sodium perborate, Citric acid, Sodiumlau- rylsulfate, Aroma Queisser Pharma, Flensburg, Germany
0.5% NaOCl Solution SH Sodium hypochlorite Aklar Kimya, Ankara, Turkey

Immersion protocol

The specimens were immersed in four cleaning solutions: CT, PT, SH, and DW. The same procedure was applied for two effervescent cleanser tablets (Corega and Protefix) prepared according to the manufacturers recommendations by adding one tablet to 200ml of warm tap water. All the specimens in each of the four groups (CT, PT, SH, and DW) group were stored in the respective solution for 8h to simulate overnight use. The solutions were renewed three times a day. At this point, the specimens were removed, washed in water, and returned to the storage media. This procedure was repeated for 120d to simulate 1 y of use. The same operator performed these steps at room temperature (i.e., between 23 and 24°C) to maintain standardization and avoid temperature variations, respectively.

Color measurements

Color measurements of the specimens before and after immersion in the various cleaning agents were obtained using a spectrophotometer (VITA Easyshade V; VitaZahnfabrik, Bad Säckingen, Germany). The color measurements of each sample were made with the sample placed on the same white background. To obtain the average color value of a sample, three measurements were made at three different places in the middle area of each specimen at a right angle to the surface of the specimen. The average values were then recorded. The measurements were performed under D65 standard illumination conditions, calibrating each measurement according to the manufacturers instructions. Color changes were measured and recorded in L* a* b*. The color change (ΔE00) was calculated using the CIEDE2000 formula.

To calculate the color change (ΔE00) values, we used previously reported 50% perceptibility (1.72) and acceptability (4.08) threshold values for denture acrylic-based resins (22).

Statistical analysis

The normality analysis of the data was performed using the Kolmogorov-Smirnov distri bution test. The data were found to have a normal distribution. The data for ΔE00 values were statis- tically analyzed using a multivariate analysis of variance, followed by multiple comparisons by a post hoc Tukeys test. The level of statistical signi- ficance was set at 0.05.

Results

The statistical analysis revealed significant differences between the average ΔE00 values. The mean ΔE00 values of all the denture base specimens are presented in Table 2 (p<0.05).

In group PA, CT (1,81±0,28) showed the lowest statistically ΔE00 value among all cleansers. Group PA-SH (3,28±0,64) and group PA-DW (2,71±0,79) showed the highest statistically ΔE00 value among SH and DW groups. PA-CT (1,81±0,28) showed the statistically lowest ΔE00 value for the PA group. ΔE00 values of all solutions in group PA were statistically higher than group HP.

In addition, all cleansers in group PA were statisti- cally higher than group AP, except for PA-CT.

In group PK, DW (1.76±0.51), which was the control group, showed the lowest ΔE00 value statistically compared to denture cleansers. Group PK-CT (2,70±0,50) was the statistically highest ΔE00 value among CT solutions. ΔE00 values of all solutions in group PK were statistically higher than group HP like group PA.

In group AP, SH (2.47±0.54) statistically the highest ΔE00 values were found compared to other cleansers. In group HP, there was no statistically significant difference between the average ΔE00 values of all solutions. In addition, ΔE00 values of all solutions in group AP were higher than group HP, but there was only a statistically significant diffe- rence between the CT and SH groups.

Table 2 The ΔE00 values of the DBPs after immersion in various denture cleansers (p<0.05). 

Groups Mean ± SD - - -
- DW CT PT SH
AP 1,59± 0,43ªᴬ 1,67 ± 0,31ªͨᴮ 1,47 ± 0,33ªͨ 2,47 ± 0,54ªᵇ,ᴬᴮ
HP 1,15 ± 0,20ᵇͨ 1,14 ± 0,23ªᵇ ͩ 1,23 ± 0,30ᵇ ͩ 1,29 ± 0,12ªͨ ͩ
PA 2,71 ± 0,79ªᵇ ͩᴬ 1,81 ± 0,28ᵇͤᴬᴮ 2,64 ± 0,85ªᵇᴮ 3,28 ± 0,64ᵇͨ ͤ
PK 1,76 ± 0,51ͨ ͩ ᴬᴮ 2,70 ± 0,50 ͨ ͩ ͤ ᴬ 2,53 ± 0,72 ͨ ͩ ᴮ 2,61 ± 0,54 ͩ ͤ

The same superscript lowercase letters indicate statistical differences within lines, and the same superscript uppercase letters indicate statistical differences within columns. SD: standard deviation.

Discussion

In this study, significant differences were detected in the color stability of PK, PA, AP, and HP samples immersed in the different denture cleaning solutions. Consequently, the null hypothesis that the denture cleansers would have no effect on the color stability of the different DBPs was rejected.

Based on a detailed literature review, only a few studies appear to have focused on color changes in PEEK material when used as a denture base. According to the results of the present study, comparison of the ΔE00 values in the various denture cleanser groups revealed the lowest mean ΔE00 value in the PK-DW group. Heimer et al. (20) examined the effect of different cleaning methods on the color stability of PK material under diffe- rent environmental conditions over a 7-d period and reported that the color stability of PK was better than that of AP and composite resin. Unlike their study, we evaluated the impact of long-term immersion in denture cleansers on color stability. As shown by the statistical analysis, the highest ΔE00 values were found in the PK group compa- red to the HP group for all cleansers (p<0.05). Similarly, the ΔE00 values of all the cleansers were lower for the other PMMA resin (AP) compared to the PK group. However, only the CT and PT groups were statistically different when compared to AP. It is possible that the different translucencies and optical properties of the DBPs tested in the present study affected the color measurements.

Similar to PEEK, polyetherketoneketone (PEKK), a high-temperature polymer, is a member of the polyaryletherketone family (1). Ozyilmaz et al. (1) evaluated the effect of denture cleansers on long-term color stability and surface topography of PA, HP, and PEKK DBPs and reported changes in these parameters in all the DBPs. It was reported that alkali peroxide-based effervescent cleansers (CT, PT) affected the color stability of PA more than PEKK and HP (1). Durkan et al. (19) evaluated the effect of denture cleansers applied for 20 d on the surface roughness, hardness, and color stability of two polyamides (Valpast and Deflex), a butadiene styrene copolymer PMMA (Rodex), and a PMMA polymer (Paladent). They reported that immersion in the denture cleansers significantly affected the surface roughness and color stability of the polya- mides (19). Although not evaluated in our study, it is known that polyamides are more susceptible to change in water absorption and surface roughness than PMMA (26). These disadvantages of polyamides are consistent with the fact that more color changes were seen in our study. In the present study, the higher ΔE00 values were found in the PA group compared to the PMMA groups (AP and HP).

AP acrylic resins have a lower degree of cross-linking than HP (27). AP acrylic resins show higher water absorption and solubility than HP resins (28). More residual monomer is observed in AP resins than HP resins (29). In addition, since AP resins contain amine accelerators, they exhibit higher solubility due to their oxidation (30). In our study, the fact that the AP group showed more color change in all cleansers compared to HP is consistent with this information.

Earlier studies reported discoloration, loss of soluble components, and water sorption in acrylic resin materials immersed in denture cleansers (13,17,18,19). The length of time immersed in the denture cleansers significantly affected the color stability of the acrylic resin materials (13). Based on the ΔE00 values, we found statistically significant color changes in all the DBPs immersed in the denture cleaning agents for 1 y of simulated use. These color changes may be the result of leaking components of the coloring material. The opacity of acrylic resin after prolonged immersion may be caused by leakage or sorption of monomers. Alkaline peroxides, available in effervescent tablets or powder form, dissolve in water and react to form a hydrogen peroxide solution, resulting in the release of oxygen. Via mechanical action, the released oxygen removes deposits on the prosthesis (18). However, it is a known fact that cleaning tablets containing sodium perborate and sodium bicarbonate increase the surface roughness of polymer-based materials (31). The cleaning tablets are colored because the released oxygen causes surface roughness (10). Davi et al.(16) reported that cleaning with alkaline chemical solutions stimulated the release of plasticizers and changed the surface properties of polymer-based denture base resins. Peracini et al. (17) reported that denture cleansers should be used carefully due to their negative effects, such as discoloration, on the physical appearance of DBPs. Additionally, it has been shown that sodium hypochlorite has a bleaching effect depending on the usage time and concentration (16). The color stability of the DBPs immersed in various denture cleaning agents in the present study differed, with values below the 50% acceptability threshold (4.08) found for all the materials. According to the results of our study, which simulated 1 y of clinical use, the denture cleansers used caused clinically acceptable discoloration of the DBPs. Daily use of denture cleansers can affect both the physical and mechanical properties of DBPs. Color stability is an indicator of aging or damage and affects the longevity of dental prostheses (13). Subsequent studies on PEEK need to be supported by investigations of the effects of other parameters, such as the surface topography, water sorption, and solubility.

The color stability of the restorations is highly proportional to their roughness (32). In addition, microbial adhesion and products in the oral environment can change the color stability (33). Ideal restorative materials should have low liquid absorption, good polishability and color stability as well as strong mechanical strength. In particular, its polishability increases color stabi lity and extends the life of the restoration (20). It is difficult for dental technicians and dentists to determine an ideal polishing method due to the lack of precise guidelines for PEEK material. Data are missing for the most appropriate PEEK polishing method and its effect on surface rough- ness and surface free energy (34). Unfilled PEEK samples were used in this study. Modification of PEEK materials with carbon and glass fibers can reduces wear with chain structures and increases physical strength (35). The addition of ceramic fillers to the polymers results in a high degree of polishability, thereby reducing plaque adhesion and providing long-term color stability (36). Polishability and color stability enable the production of partial or complete removable prostheses that are more stable and satisfactory result (1).

The present study had a number of limitations. The samples were tested under conditions that may not reflect actual clinical conditions. The tests also did not fully simulate parameters in the oral environment, such as temperature, moisture, and denture biofilm, which may have implica- tions for the color change measurements. Another limitation of this study was that the lack of trans- lucency of PEEK material may also have influenced the color stability measurements.

Conclusion

Within the limitations of this in vitro study, we conclude that overnight use of denture cleaning solutions with different chemical compositions caused color changes in various types of DBPs, including PEEK, but these changes were within acceptable limits. To validate the results of this study, as well as laboratory studies, clini- cal studies are needed to investigate the effect of different denture cleansers on the color stability of PEEK.

Funding

The study was self-funded.

Conflicts of interest statement

No conflict of interest

Acknowledgments

This research did not receive any speci- fic grant from funding agencies in the public, commercial, or not-for-profit sectors.

References

Ozyilmaz O.Y., Kara O., Akin C. Evaluation of various denture cleansers on color stability and surface topography of polyetherketone- ketone, polyamide, and polymethylmethac- rylate. Microsc Res Tech. 2021; 84 (1): 3-11. [ Links ]

Zafar M.S. Prosthodontic Applications of Polymethyl Methacrylate (PMMA): An Update. Polymers (Basel). 2020; 12 (10): 2299. [ Links ]

Yunus N., Rashid A.A., Azmi L.L., Abu-Hassan M.I. Some flexural properties of a nylon denture base polymer. J Oral Rehabil. 2005; 32 (1): 65-71. [ Links ]

Vojdani M., Giti R. Polyamide as a Denture Base Material: A Literature Review. J Dent (Shiraz). 2015; 16 (1 Suppl): 1-9. [ Links ]

Schwitalla A., Muller W.D. PEEK dental implants: a review of the literature. J Oral Implantol. 2013; 39 (6): 743-749. [ Links ]

Wiesli M.G., Özcan M. High-Performance Polymers and Their Potential Application as Medical and Oral Implant Materials: A Review. Implant Dent. 2015; 24 (4): 448-457. [ Links ]

Schwitalla A. D., Spintig T., Kallage I., Muller W.D. Flexural behavior of PEEK materials for dental application. Dent Mater. 2015; 31 (11): 1377-1384. [ Links ]

Takabayashi Y. Characteristics of denture thermoplastic resins for non-metal clasp dentures. Dent Mater J. 2010; 29 (4): 353-361. [ Links ]

Zoidis P., Papathanasiou I., Polyzois G. The Use of a Modified Poly-Ether-Ether- Ketone (PEEK) as an Alternative Framework Material for Removable Dental Prostheses. A Clinical Report. J Prosthodont. 2016; 25 (7): 580-584. [ Links ]

Machado A.L., Breeding L.C., Vergani C.E., da Cruz Perez L.E. Hardness and surface roughness of reline and denture base acrylic resins after repeated disinfection procedures. J Prosthet Dent. 2009; 102 (2): 115-22. [ Links ]

Alam M, Jagger R., Vowles R., Moran J. Comparative stain removal properties of four commercially available denture cleaning products: an in vitro study. Int J Dent Hyg. 2011; 9 (1): 37-42. [ Links ]

Felipucci D.N., Davi L.R., Paranhos H.F., Bezzon O.L., Silva R.F., Pagnano V.O. Effect of different cleansers on the surface of removable partial denture. Braz Dent J. 2011; 22 (5): 392-7. [ Links ]

Hong G., Murata H., Li Y., Sadamori S., Hamada T. Influence of denture cleansers on the color stability of three types of denture base acrylic resin. J Prosthet Dent. 2009; 101 (3): 205-13. [ Links ]

Silva P.M., Acosta E.J., Jacobina M., Pinto L. de R., Porto V.C. Effect of repeated immer- sion solution cycles on the color stability of denture tooth acrylic resins. J Appl Oral Sci. 2011; 19 (6): 623-627. [ Links ]

Piskin B., Sipahi C., Akin H. Effect of diffe- rent chemical disinfectants on color stability of acrylic denture teeth. J Prosthodont. 2014; 23 (6): 476-483. [ Links ]

Davi L.R. , Peracini A., Ribeiro N. de Q., Soares R.B., da Silva CH., Paranhos H. de F., de Souza R.F. Effect of the physical properties of acrylic resin of overnight immersion in sodium hypochlorite solution. Gerodontology. 2010; 27 (4): 297-302. [ Links ]

Peracini A. , Machado Andrade I., Oliveira V.C., Macedo A.P., Silva-Lovato CH., Oliveira Pagnano V., Watanabe E., Oliveira Paranhos H.F. Antimicrobial action and long- term effect of overnight denture cleansers. Am J Dent. 2017 Apr; 30 (2): 101-108. [ Links ]

Peracini A. , Davi L.R. , de Queiroz Ribeiro N., de Souza R.F., Lovatoda Silva CH. , de Freitas Oliveira Paranhos H. Effect of denture cleansers on physical properties of heat-polymerized acrylic resin. J Prosthodont Res. 2010; 54 (2): 78-83. [ Links ]

Durkan R., Ayaz E.A., Bagis B., Gurbuz A., Ozturk N., Korkmaz F.M. Compara tive effects of denture cleansers on physi- cal properties of polyamide and polymethyl methacrylate base polymers. Dent Mater J. 2013; 32 (3): 367-375. [ Links ]

Heimer S., Schmidlin P.R., Stawarczyk B. Discoloration of PMMA, composite, and PEEK. Clin Oral Investig. 2017; 21 (4): 1191-1200. [ Links ]

Alp G., Johnston W.M., Yilmaz B. Optical properties and surface roughness of prepoly- merized poly(methyl methacrylate) denture base materials. J Prosthet Dent. 2019; 121 (2): 347-352. [ Links ]

Ren J., Lin H., Huang Q., Zheng G. Determining color difference thresholds in denture base acrylic resin. J Prosthet Dent. 2015;114(5):702-708. [ Links ]

Luo M.R., Cui G., Rigg B. The development of the CIE 2000 color-difference formula: CIEDE2000. Color Res Appl. 2001; 26 (5): 340-350. [ Links ]

Wee A.G., Lindsey D.T., Shroyer K.M., Johnston W.M. Use of a porcelain color discrimination test to evaluate color difference formulas. J Prosthet Dent. 2007; 98 (2): 101-109. [ Links ]

Polychronakis N., Lagouvardos P., Polyzois G. , Sykaras N., Zoidis P. Color changes of polyetheretherketone (PEEK) and polyoxy- methelene (POM) denture resins on single and combined staining/cleansing action by CIELab and CIEDE2000 formulas. J Prosthodont Res. 2020; 64 (2): 159-166. [ Links ]

Goiato M.C., Santos D.M., Haddad M.F., Pesqueira A.A. Effect of accelerated aging on the microhardness and color stability of flexi- ble resins for dentures. Braz Oral Res. 2010; 24 (1): 114-119. [ Links ]

Arima T., Murata H. , Hamada T. Properties of highly cross-linked autopolymerizing reline acrylic resins. J Prosthet Dent. 1995; 73 (1): 55-59. [ Links ]

Purnaveja S., Fletcher A.M., Ritchie G.M., Amin W.M., Moradians S., Dodd A.W. Colour stability of two self curing denture base materials. Biomaterials. 1982; 3 (4): 249-250. [ Links ]

Austin A.T., Basker R.M. Residual monomer levels in denture bases. The effects of varying short curing cycles. Br Dent J. 1982; 153 (12): 424-426. [ Links ]

Memon M.S., Yunus N. , Razak A.A. Some mechanical properties of a highly cross- linked, microwave-polymerized, injection-molded denture base polymer. Int J Prosthodont. 2001; 14 (3): 214-218. [ Links ]

Ozyilmaz O.Y. , Akin C. Effect of cleansers on denture base resins structural properties. J Appl Biomater Funct Mater. 2019; 17 (1): 2280800019827797. [ Links ]

Turkun L.S., Leblebicioğlu E.A. Stain reten- tion and surface characteristics of posterior composites polished by one-step systems. Am J Dent. 2006; 19 (6): 343-347. [ Links ]

Costa M.T., Dorta M.L., Ribeiro-Dias F., Pimenta F.C. Biofilms of black tooth stains: PCR analysis reveals presence of Streptococcus mutans. Braz Dent J. 2012; 23 (5): 555-558. [ Links ]

Heimer S. , Schmidlin P.R. , Roos M., Stawarczyk B. Surface properties of polyetherether- ketone after different laboratory and chairside polishing protocols. J Prosthet Dent. 2017; 117 (3): 419-425. [ Links ]

Kurtz S.M., Devine J.N. PEEK biomaterials in trauma, orthopedic, and spinal implants. Biomaterials. 2007; 28 (32): 4845-4869. [ Links ]

Attia M.A., Shokry T.E. Effect of different fabrication techniques on the marginal preci- sion of polyetheretherketone single-crown copings. J Prosthet Dent. 2020; 124 (5): 565. e1-565.e7. [ Links ]

Received: March 16, 2021; Accepted: May 04, 2021; pub: June 09, 2021

Creative Commons License This is an open-access article distributed under the terms of the Creative Commons Attribution License